Graphic Finishing Partners GFP Pressure Sensitive Mounting Adhesives
Company Page
Click Here
Product Details Page
Click Here
Film Products Brochure
Click Here
Film Products Summary
Click Here
Mounting Adhesives And Kraft Paper
Click Here
Economy Film Roll Sizes
Click Here
Intermediate Film Roll Sizes
Click Here
Mounting Adhesive Roll Sizes
Click Here
Intermediate Print Media Roll Sizes
Click Here
Thermal Film Roll Sizes
Click Here
Product Data Sheet
Click Here
Product Data Sheet
Click Here
Product Data Sheet
Click Here
Gfp Mounting Adhesive Products
Flawless finish. Flexible applications. Superior Bond.
Gfp Mounting Adhesive Products are designed for the Graphic Arts Industry to provide quality, long-lasting performance for a wide range of digital print mounting applications. Clear and White Mount have 1 mil (25 ?) pressure-sensitive permanent solvent acrylic adhesive, with neutral pH value of 7. 0 applied to both sides of a carrier substrate.
Clear Mount – 1 mil (25?) Clear Polyester carrier coated two sides with clear solvent adhesive: one adheres to the back of a printed image, the other to a mounting board. It bonds the image to paper covered boards like Gatorfoam®, but forms a superior bond to low energy plastic surfaces like polystyrene, Sintra®, Gatorboard, and Ultraboard™. The single release liner is 75# (105 gsm) white paper coated both sides with moisture stabilizing PE and siliconized on the release side. Recommended for decaling printed images or pre-coating boards prior to mounting.
White Mount – 3 mil (75?) white Polypropylene carrier with 87% opacity reduces color shift when mounting to dark surfaces like Black Gatorboard. The carrier is coated two sides with 1 mil (25?) permanent aggressive water-based acrylic adhesive: one adheres to the back of the printed image, the other to all styles of mounting boards. The single release liner is 3 mil (76?) white paper coated both sides with moisture stabilizing PE and siliconized on the release side. Used for decaling printed images or pre-coating boards prior to mounting, it blocks bleed-through from images on dark mounting boards.
Front Mount – 1.4 mil (36?) Optically clear Polyester carrier coated two sides with clear permanent solvent adhesive: one side adheres to the front of the image, the other to the inside of a clear substrate. In this face mounting process, the image is viewed through a clear substrate like Plexiglas®, acrylic, polycarbonate, and glass. Front Mount has two 1.4 mil (36?) silicone-coated Polyester liners to ensure smooth adhesive surface without debris. It is used to display digital images or photographs and for backlit display applications. Recommended for promotional advertising, POP displays, touch screens, window graphics, or trade show exhibits requiring a see-through transparent surface.
Clear Mounting Adhesive (MAC)
Base Carrier: 0.9 mil (23?) Clear Polyester (PET)
Adhesive #1: 1.0 mil (25?) Permanent Clear Solvent-based Acrylic
Adhesive #2: 1.0 mil (25?) Permanent Clear Solvent-based Acrylic
Liner: 75# (110gsm) two side PE coated and siliconized white Kraft paper
pH-value: approximately 7.0 neutral
Durability: Up to 2 years, vertical exposure outdoors
White Mounting Adhesive (WMA)
Base Carrier: 3.0 mil (75?) White Biaxially oriented Polypropylene
Adhesive #1: 1.0 mil (25?) Permanent Clear Water-based Acrylic
Adhesive #2: 1.0 mil (25?) Permanent Clear Water-based Acrylic
Liner: 60# (88gsm) two side PE coated and siliconized white Kraft paper
pH-value: approximately 7.0 neutral
Opacity: 87%
Durability: Up to 2 years, vertical exposure outdoors
Front Mounting Adhesive (MAF)
Base Carrier: 1.4 mil (36?) Optically Clear Polyester (PET)
Adhesive #1: 1.0 mil (25?) Permanent Clear Solvent-based Acrylic
Adhesive #2: 1.0 mil (25 ?) Permanent Clear Solvent-based Acrylic
Liner #1: 1.4 mil (36?) Siliconized Clear Polyester (PET)
Liner #2: 1.4 mil (36?) Siliconized Clear Polyester (PET)
pH-value: approximately 7.0 neutral
Durability: Up to 2 years, vertical exposure outdoors
Mounting Adhesive is suitable for short to medium term indoor or outdoor signage on flat or slightly curved surfaces with vertical exposure and application temperatures of 40° F to 176° F. Bond strength is dependent upon the amount of adhesive to the mounting surface contact that is developed. Firm application pressure and moderate heat will assist the adhesive in developing contact with the mounting surface. For optimum adhesive, the mounting surface must be clean and dry.
Durability estimates do not apply to the printed image. They are based on accelerated aging tests and outdoor exposure, under conditions experienced in vertical exposure and in “normal” temperate climates. Exposure to severe humidity and ultraviolet light as in Southern States or desert regions will cause rapid deterioration. This also applies to polluted areas, high altitude, horizontal and/ or south-facing exposure. Because of these varying climate conditions there is no standard outdoor life durability; it is only a reference for choosing the proper product.
Important Notice
Gfp products are warranted to be free from defects in material and workmanship (see Gfp Product Warranty statement). Product information is based on research the company believes to be reliable; however, such information is given without guarantee and does not constitute a warranty. Purchasers should undertake their own evaluation of the product prior to use to independently determine the suitability of the product to their specific application and the purchaser shall assume all risks regarding such use.
Product Data Sheet
Clear Mounting Adhesive (MAC)
Product Description Polyester carrier/ Acrylic copolymer/ Siliconized paper
Base Material Carrier: Clear polyester
Base Material Carrier: Thickness 0.9 mil (23?) ± 5%
Base Material Carrier: Weight 33gsm ± 5%
Adhesive #1: Permanent clear Solvent-based Acrylic
Adhesive #1: pH-value approx. 7.0 Neutral
Adhesive #1: Thickness 1.0 mil (25?) ± 5
Adhesive #1: 180° Peel Adhesion (kg/inch) (method: PSTC-1) 1kg/inch
Adhesive #1: 0° Shear strength (hr./inch) (method: PSTC-7) 54hrs/inch
Adhesive #2: Permanent clear Solvent-based Acrylic
Adhesive #2: pH-value approx. 7.0 Neutral
Adhesive #2: Thickness 1.0 mil (25?) ± 5
Adhesive #2: 180° Peel Adhesion (kg/inch) (method: PSTC-1) >1kg/inch
Adhesive #2: 0° Shear strength (hr./inch) (method: PSTC-7) >54hrs/inch
Release Liner: Type of Release Liner Two Side Siliconized Paper
Release Liner: Release Liner Weight (gsm) 75# (110gsm) ± 5%
Release Liner: Number of sides PE coated 2
Heat Resistance: Temperature range +5? C to 80? C/ 40? F to 176? F
Application temperature: Temperature range +15? C to 50? C / 59? F to 122? F
Storage conditions: 18? C to 25? C / 64? F to 77? F ; 50-60% relative humidity
Shelf life: 1 year when stored under proper conditions in original package
Durability: Up to 2 years, vertical exposure
Front Mounting Adhesive (MAF)
Product Description Clear Polyester carrier/ Acrylic copolymer adhesive/ Siliconized Polyester liners
Base Material Carrier: Optically clear Polyester
Base Material Carrier: Thickness 1.4 mil (36?) ± 5%
Base Material Carrier: Weight 50 gsm ± 5%
Adhesive #1: Permanent clear Solvent-Based Acrylic
Adhesive #1: pH value approx. 7.0 Neutral
Adhesive #1: Thickness 1.0 mil (25?) ± 5
Adhesive #1: 180° Peel Adhesion (kg/inch) (method: PSTC-101) 1kg/inch
Adhesive #1: 0° Shear strength (hr./inch) (method: PSTC-107) 54hrs/inch
Adhesive #2: Permanent clear Solvent-Based Acrylic
Adhesive #2: pH value approx. 7.0 Neutral
Adhesive #2: Thickness 1.0 mil (25?) ± 5
Adhesive #2: 180° Peel Adhesion (kg/inch) (method: PSTC-101) >1kg/inch
Adhesive #2: 0° Shear strength (hr./inch) (method: PSTC-107) >54hrs/inch
Release Liner #1: Type of Release Liner Siliconized clear polyester
Release Liner #1: Thickness of Release Liner .9 mil (23?) ± 5%
Release Liner #2: Type of Release Liner Siliconized clear polyester
Release Liner #2: Thickness of Release Liner .9 mil (23?) ± 5%
Heat Resistance: Temperature range +15? C to 35? C/ 59? F to 95? F
Storage conditions: 18? C to 23? C / 66? F to 74? F; 50% relative humidity
Shelf life: 1 year when stored at 18? to 25?C ( 60? to 80? F) at 40-65% humidity in original package
Durability: Up to two years, vertical exposure outdoors
White Mounting Adhesive - (WMA)
Product Description White Polypropylene carrier (BOPP)/Acrylic copolymer/Siliconized paper
Base Material Carrier: Polypropylene White BOPP
Base Material Carrier: Thickness 3.0 mil (75?) ± 5%
Base Material Carrier: Weight 45 g/m² ± 5%
Base Material Carrier: Opacity 87%
Base Material Carrier: Tensile Strength - Machine Direction (MD) (method: ASTM D-638) 7,977 PSI
Base Material Carrier: Tensile Strength - Transverse Direction (TD) (method: ASTM D-638) 16,244 PSI
Base Material Carrier: Shrinkage - Machine Direction (MD) (method: ASTM D-1204) 0%
Base Material Carrier: Shrinkage - Transverse Direction (TD) (method: ASTM D-1204) 0%
Adhesive #1: Permanent clear Water-based - Polyacrylate dispersion
Adhesive #1: pH-value approx. 7.0 Neutral
Adhesive #1: Thickness 1.0 mil (25?) ± 5%)
Adhesive #1: Adhesive Strength - 180° Peel (method: AFERA 4001) (N/25 mm) 10 min >7 24 hrs. > 11
Adhesive #2: Permanent clear Water-based - Polyacrylate dispersion
Adhesive #2: pH-value approx. 7.0 Neutral
Adhesive #2: Thickness 1.0 mil (25?) ± 5%)
Adhesive #2: Adhesive Strength - 180° Peel (method: AFERA 4001) (N/25 mm) 10 min >7 24 hrs. > 11
Release Liner: Bleach White Kraft Paper Silicone 2-side coated
Release Liner: Thickness 3.0 mil (75?) ±5
Release Liner: Release Liner Weight 60# (88 g/m²) ± 3%
Release Liner: Removal Force ( speed 300 mm/min.) 20-45 mN/cm
Release Liner: Tear Resistance - Machine Direction (MD) (method: ASTM D-470) >55 N/mm²
Release Liner: Tear Resistance - Transverse Direction (TD) (method: ASTM D-470) >110 N/mm²
Release Liner: Tear Resistance - Machine Direction (MD) (method: DIN EN 21974) 245 mN
Release Liner: Tear Resistance - Transverse Direction (TD) (method: DIN EN 21974) 265 mN
Release Liner: Tensile Strength - Machine Direction (MD) (method: EN ISO 1924-2) 5 kN/m
Release Liner: Tensile Strength - Transverse Direction (TD) (method: EN ISO 1924-2) 2.3 kN/m
Processing Temperature: Processing Temperature range 41? to 104? F (4? to 40? C)
Heat Resistance: Application Temperature range 32° to 212° F (0° - 100° C)
Storage conditions: 64? to 77? F (18? to 25? C); 40-65% relative humidity
Shelf life: 1 year when stored at 18? to 25?C ( 60? to 80? F) at 40-65% humidity in original package
Durability: Up to 2 years, vertical exposure