Graphic Finishing Partners GFP Pressure Sensitive Over-Laminates Polymeric UV
Company Page
Click Here
Product Details Page
Click Here
Film Products Brochure
Click Here
Film Products Summary
Click Here
Mounting Adhesives And Kraft Paper
Click Here
Economy Film Roll Sizes
Click Here
Intermediate Film Roll Sizes
Click Here
Mounting Adhesive Roll Sizes
Click Here
Intermediate Print Media Roll Sizes
Click Here
Thermal Film Roll Sizes
Click Here
Product Data Sheet
Click Here
Product Data Sheet
Click Here
Product Data Sheet
Click Here
Intermediate PSA Overlaminate Films
These Polymeric PVC based films have added UV inhibitors for indoor or medium-term outdoor graphics for up to 5 years durability with vertical exposure under normal conditions. Each soft calendared PVC has more complex plasticizers to improve outdoor durability and minimize shrinkage from plasticizer migration. The PVC is coated with 1 mil (25 ?) permanent solvent acrylic adhesive. This adhesive is protected by a 70# (105 gsm) white paper release liner coated signage or high-end indoor graphics requiring extra protection.
Gloss –Reflective 3.2 mil (80 ?) PVC produces rich depth of color, image contrast and vibrancy. (Gloss level 100 @ 60° reflection) Longer term outdoor banners, commercial signs, displays and flat surface vehicle graphics
Luster –Low reflection 3.2 mil (80 ?) PVC for less glare and better viewing from all angles. (Gloss level 30 @ 60° reflection) Promotional displays, event signage
Matte –Flat surface 3.2 mil (80 ?) PVC absorbs light for a softer look with a muted color palette. (Gloss level 15 @ 60° reflection) Trade show graphics, POP display
Polymeric PVC laminating film is suited for medium to long term indoor or outdoor signage on flat or slightly curved surfaces with vertical exposure and application temperatures of 40° F to 176° F. Polymeric products are more suited for outdoor applications than the Monomeric because they have higher quality plasticizers and more UV blocking additives, which evaporate more slowly than Monomeric PVC. Durability of the laminate (whether Monomeric or Polymeric) depends on proper drying/curing/ outgassing of the ink. Printed PVC must be allowed to dry for 24-48 hours at 70° F prior to lamination to allow residual solvent to evaporate. Failure to do so may result in delamination, tunneling, and shrinkage of the PVC and or adhesive failure.
The amount of dry time required is a function of the amount of ink applied, the image printed, relative humidity, printing conditions, etc. and all prints are not the same nor dry at the same rate. There may still be solvent in the ink that has not completely dried at the time of lamination. Although all PVC outgases, in some cases this process is accelerated by the presence of excess solvent in the ink and heat from high UV exposure.
These Durability estimates apply only to the laminating film not to the printed image. They are based on accelerated aging tests and outdoor exposure, under conditions experienced in vertical exposure and in “normal” temperate climates. Exposure to severe humidity and ultraviolet light as in Southern States or desert regions will cause rapid deterioration. This also applies to polluted areas, high altitude, horizontal and/ or south-facing exposure where durability may be divided by 2. Because of these varying climate conditions there is no standard outdoor life durability; it is only a reference for choosing the proper product.
Important Notice
Gfp products are warranted to be free from defects in material and workmanship (see Gfp Product Warranty statement). Product information is based on research the company believes to be reliable; however, such information is given without guarantee and does not constitute a warranty. Purchasers should undertake their own evaluation of the product prior to use to independently determine the suitability of the product to their specific application and the purchaser shall assume all risks regarding such use.
General Specifications:
Intermediate UV 3 mil PVC Film - Gloss
Intermediate UV 3 mil PVC Film - Luster
Intermediate UV 3 mil PVC Film - Matte
Product Description: PVC film/ Acrylic copolymer/ Siliconized paper
Face Material: Calendared Polymeric Polyvinyl Chloride
Face Material: Thickness 3.2 mil (80?) ± 5%
Face Material: Weight (gsm) 105gsm ± 5%
Adhesive: Permanent clear Solvent-based Acrylic
Adhesive: pH-value approx. 7.0 Neutral
Adhesive: Coating thickness 1.0 mil (25?) ± 5%
Adhesive: 180° Peel Adhesion (kg/inch) (method: PSTC-1) >1kg/inch
Adhesive: 0° Shear strength (hr./inch) (method: PSTC-7) >54hrs/inch
Release Liner: White Siliconized Paper
Release Liner: Weight 70# (105gsm) ± 5%
Heat Resistance: Temperature range +5? C to 80? C / 40? F to 176? F
Application temperature: Temperature range +15? C to 50? C / 59? F to 122? F
Storage conditions: 18? C to 25? C / 64? F to 77? F; 50-60% relative humidity
Shelf life: 1 year when stored under proper conditions in original package
Durability: Up to 5 years, vertical exposure outdoors
Specific Specifications:
GLOSS - Face Material: Gloss Level (method: ASTM D-523 - 60?) > 90 GU
LUSTER - Face Material: Gloss Level (method: ASTM D-523 - 60?) 25-40 GU
MATTE - Face Material: Gloss Level (method: ASTM D-523 - 60?) 10-20 GU